安定き裂先端近傍におけるボイドの形成について |
|
言語 |
ja |
| タイトル |
|
|
タイトル |
Void Formation around a Stably Growing Crack Tip |
|
言語 |
en |
| 言語 |
|
|
言語 |
jpn |
| 資源タイプ |
|
|
資源タイプ |
journal article |
| 著者 |
小栗, 久和
本間, 寛臣
平河, 昌己
OGURI, Hisakazu
HOMMA, Hiroomi
HIRAKAWA, Masami
|
| 抄録 |
|
|
内容記述タイプ |
Abstract |
|
内容記述 |
Voids formed around the tip of a stably growing crack in SM50A steel were observed in every 10 μm thickness of the specimen through an optical microscope. The results showed that the shape of voids was disklike, the thickness of which was in the direction of the specimen thickness. The void dimensions increased with the J-integral level, maintaining a similar configuration. The density of void distribution ahead of the stable crack became higher as the J-integral level increased, but it was so low that coalescence of the voids and the crack resulted in a zigzag crack front. |
| 内容記述 |
|
|
内容記述タイプ |
Other |
|
内容記述 |
・rights：日本機械学会
・rights：本文データは学協会の許諾に基づきCiNiiから複製したものである
・relation：isVersionOf：http://ci.nii.ac.jp/naid/110002377936/ |
| bibliographic_information |
日本機械学會論文集. A編
en : Transactions of the Japan Society of Mechanical Engineers. A
巻 56,
号 523,
p. 469-473,
発行日 1990-03-25
|
| 出版者 |
|
|
出版者 |
一般社団法人日本機械学会 |
| item_10001_source_id_9 |
|
|
収録物識別子タイプ |
PISSN |
|
収録物識別子 |
03875008 |
| 関連サイト |
|
|
|
識別子タイプ |
URI |
|
|
関連識別子 |
http://ci.nii.ac.jp/naid/110002377936/ |
|
|
関連名称 |
CiNii |
| 出版タイプ |
|
|
出版タイプ |
VoR |
| キーワード |
|
|
主題 |
Ductile_Fracture |
| キーワード |
|
|
主題 |
Crack_Propagation |
| キーワード |
|
|
主題 |
J-integral_Stable_Crack_Growth |
| キーワード |
|
|
主題 |
Voids |
| キーワード |
|
|
主題 |
Ductile_Fracture |
| キーワード |
|
|
主題 |
Crack_Propagation |
| キーワード |
|
|
主題 |
J-integral_Stable_Crack_Growth |
| キーワード |
|
|
主題 |
Voids |
n03875008-0056-469 (318.1 kB)
.png)